PVDC Polyvinylidene Chloride
LEGEND
A = amorphous - Cr = crystalline - C = clear - E = excellent - G = good - P = poor - O = opaque - T = translucent-
R = Rockwell - S = Shore
STRUCTURE: Cr
SPECIFIC DENSITY: 1.7
WATER ABSORBTION RATE (%): 0.1
ELONGATION (%): 250
TENSILE STRENGTH (psi): 4300
COMPRESSION STRENGTH (psi): 8000
FLEXURAL STRENGTH (psi): 5800
FLEXURAL MODULUS (psi): 72500
IMPACT (IZOD ft. lbs/in): 12.5
HARDNESS: R55
FABRICATION
- BONDING: G
- ULTRASONIC WELDING: G
- MACHINING: P
DEFLECTION TEMPERATURE (deg. F)
- @ 66 psi: 158
- @ 264 psi: 140
UTILZATION TEMPERATURE (deg. F)
- min:
- max: 175
MELTING POINT (deg. F): 169
COEFFICIENT OF EXPANSION: 0.00011
ARC RESISTANCE:
DIELECTRIC STRENGTH (kV/mm):
TRANSPARENCY: C
UV RESISTANCE: P
CHEMICAL RESISTANCE
- ACIDS: P
- ALKALIS: E
- SOLVENTS: P