PP/Talc Polypropylene 40% Talc Filled
LEGEND
A = amorphous - Cr = crystalline - C = clear - E = excellent - G = good - P = poor - O = opaque - T = translucent-
R = Rockwell - S = Shore
STRUCTURE: Cr
SPECIFIC DENSITY: 1.22
WATER ABSORBTION RATE (%): 0.02
ELONGATION (%): 18
TENSILE STRENGTH (psi): 4000
COMPRESSION STRENGTH (psi): 5800
FLEXURAL STRENGTH (psi): 6800
FLEXURAL MODULUS (psi): 464000
IMPACT (IZOD ft. lbs/in): 2.8
HARDNESS: R95
FABRICATION
- BONDING: P
- ULTRASONIC WELDING: P
- MACHINING: E
DEFLECTION TEMPERATURE (deg. F)
- @ 66 psi: 230
- @ 264 psi: 175
UTILZATION TEMPERATURE (deg. F)
- min: -14
- max: 275
MELTING POINT (deg. F): 338
COEFFICIENT OF EXPANSION: 0.000037
ARC RESISTANCE: 130
DIELECTRIC STRENGTH (kV/mm): 22
TRANSPARENCY: O
UV RESISTANCE: P
CHEMICAL RESISTANCE
- ACIDS:
- ALKALIS:
- SOLVENTS:
More on Polypropylene
BACK